Corrosion deterioration and equivalent relationship between natural exposure and salt spray accelerated environment of reinforced concrete
更新时间：2025-05-26

    • Corrosion deterioration and equivalent relationship between natural exposure and salt spray accelerated environment of reinforced concrete

    • “In the study of reinforced concrete degradation in western saline soil areas, experts established a degradation model based on the Weibull distribution function, revealing the degradation laws under indoor acceleration and natural exposure environments, providing a solution to the problem of reinforced concrete degradation in saline soil areas.”
    • Journal of Jilin University(Engineering and Technology Edition)   Vol. 54, Issue 2, Pages: 494-505(2024)
    • 作者机构：

      1.兰州理工大学 土木工程学院，兰州 730050

      2.兰州理工大学 西部土木工程防灾减灾教育部工程研究中心，兰州 730050

    • DOI：10.13229/j.cnki.jdxbgxb.20220414    

      CLC： TU528.1

    • Received：14 April 2022，

      Published：01 February 2024

    移动端阅览

  • FENG Qiong,TIAN Hao-zheng,QIAO Hong-xia,et al.Corrosion deterioration and equivalent relationship between natural exposure and salt spray accelerated environment of reinforced concrete[J].Journal of Jilin University(Engineering and Technology Edition),2024,54(02):494-505. DOI： 10.13229/j.cnki.jdxbgxb.20220414.

  •  
  •  

0

Views

6

下载量

0

CSCD

Alert me when the article has been cited
提交
Tools
Download
Export Citation
Share
Add to favorites
Add to my album

Related Articles

Review on strengthening technology of recycled concrete aggregate and its effect on performance of recycled aggregate concrete
Probabilistic analysis of rebar rust in concrete under marine environment
The development of Fayetteville shale play and its implications
Distribution characteristics and reservoir control significance of sandstone transporting layers in Shahejie Formation in southern slope area of Qikou Sag, Bohai Bay Basin
A new method for identifying gas-water layer in tight sandstone gas reservoirs： Case Study of Su76 well area

Related Author

HE Zi-ming
SHEN Ai-qin
WANG Lu-sheng
GUO Yin-chuan
HE Jiang-fei
Jia-chun WANG
Pei-yu YAN

Related Institution

School of Civil and Architectural Engineering， Liaoning University of Technology
School of Highway， Chang'an University
Department of Civil Engineering, Xiamen University of Technology
Department of Civil Engineering, Tsinghua University
0